Bambu stuðningsefni fyrir PLA - 500gr.
Nýtt stuðningsefni fyrir PLA frá Bambu Lab
Bambu Support for PLA is fully compatible with all Bambu Lab PLA filaments and Bambu Lab printers, offering effortless peel-off removal, smooth interface quality, with reliable performance. It eliminates the need for post-processing, saving time while delivering flawless results. All at a budget-friendly price. Upgrade…
Nýtt stuðningsefni fyrir PLA frá Bambu Lab
Bambu Support for PLA is fully compatible with all Bambu Lab PLA filaments and Bambu Lab printers, offering effortless peel-off removal, smooth interface quality, with reliable performance. It eliminates the need for post-processing, saving time while delivering flawless results. All at a budget-friendly price. Upgrade your 3D printing experience today!
With optimized support interface settings* in Bambu Studio, Bambu Support for PLA delivers an ultra-smooth contact surface that protects intricate details as if untouched. Perfect for delicate designs, overhangs, and bridges, it ensures premium quality from start to finish.
* 0mm top interface spacing and 0mm Z-distance settings
Accessory Compatibility
General information
| Recommended | Not Recommended | |
| Build Plate | Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate | / |
| Hotend | All Size / Material | / |
| Bambu Liquid Glue / Glue Stick | Bambu Liquid Glue / Glue Stick | / |
| Recommended Printing Settings | ||
| Drying Settings (Blast Drying Oven) | 55 °C, 8 h | |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) | |
| Nozzle Temperature | 220 - 230 °C | |
| Bed Temperature (with Glue) | 35 - 45 °C | |
| Printing Speed | < 200 mm/s | |
| Physical Properties | ||
| Density | 1.33 g/cm³ | |
| Vicat Softening Temperature | N / A | |
| Heat Deflection Temperature | N / A | |
| Melting Temperature | 190 °C | |
| Melt Index | 13.6 ± 1.2 g/10 min |
Shop here
-
3D Verk
The information listed is subject to change without notice. Contents, terms and conditions on vendor's web sites apply.